Osteoblast Maturation and New Bone Formation in
Response to Titanium Implant Surface Features Are
Reduced With Age
Rene Olivares-Navarrete, 1 * Andrew L Raines, 1,2 * Sharon L Hyzy, 1 Jung Hwa Park, 1 Daphne L Hutton, 1
David L Cochran , 3 Barbara D Boyan , 1 and Zvi Schwartz 1,3
1
Parker H. Petit Institute for Bioengineering and Bioscience, Georgia Institute of Technology, Atlanta, GA, USA
St. Joseph’s Translational Research Institute, Atlanta, GA, USA
3
University of Texas Health Science Center at San Antonio, San Antonio, TX, USA
2
ABSTRACT
The surface properties of materials contribute to host cellular response and play a significant role in determining the overall success or failure of an implanted biomaterial. Rough titanium (Ti) surface microtopography and high surface free energy have been shown to enhance osteoblast maturation in vitro and increase bone formation in vivo. Whereas the surface properties of Ti are known to affect osteoblast response, host bone quality also plays a significant role in determining successful osseointegration. One factor affecting host bone quality is patient age. We examined both in vitro and in vivo whether response to Ti surface features was affected by animal age.
Calvarial osteoblasts isolated from 1-, 3-, and 11-month-old rats all displayed a reduction in cell number and increases in alkaline phosphatase–specific activity and osteocalcin in response to increasing Ti surface microtopography and surface energy. Further, osteoblasts from the three ages examined displayed increased production of osteocalcin and local factors osteoprotegerin, vascular endothelial growth factor (VEGF)-A, and active transforming growth factor (TGF)-b1 in response to increasing Ti surface roughness and surface energy. Latent TGF-b1 only increased in cultures of osteoblasts from 1- and 3-month-old rats. Treatment with the systemic osteotropic hormone 1a,25(OH)2D3 further enhanced the response of osteoblasts to Ti surface features for all three age groups. However, osteoblasts derived from 11-month-old animals had a reduced response to 1a,25(OH)2D3 compared to osteoblasts derived from 1-or
3-month-old animals. These results were confirmed in vivo. Ti implants placed in the femoral intramedullary canal of old (9-month-old) mice yielded lower bone-to-implant contact and neovascularization in response to Ti surface roughness and energy compared to younger (2-month-old) mice. These results show that rodent osteoblast maturation in vitro as well as new bone formation in vivo is reduced with age. Whether comparable age differences exist in humans needs to be determined. ß 2012 American Society for Bone and
Mineral Research.
KEY WORDS: OSTEOBLASTS; AGE; MICROSTRUCTURED TITANIUM; OSSEOINTEGRATION; 1,25-DIHYDROXYVITAMIN D3
Introduction
T
he surface properties of materials and the quality of the bone contribute to host cellular response and ultimately determine the overall success or failure of an implanted biomaterial. Cells interact with the surface of a material through an adsorbed layer of proteins, ions, sugars, and lipids present in the blood and tissue fluid. Surface properties including topography, surface energy, chemistry, and surface charge are largely responsible for this interaction.(1–3)
In vitro studies show that modifications to titanium (Ti) substrate microarchitecture have effects on the attachment and differentiation of osteoblast-like cells, including MG63 and
MC3T3-E1 cell lines, as well as fetal rat calvarial cells and normal human osteoblasts.(4) On micron- and submicron-scale rough Ti substrates, cell proliferation is decreased and differentiation is increased, as these cells display changes in alkaline phosphatase specific activity and increased osteocalcin production.(5) Further,
MG63 osteoblast-like cells cultured on these rough Ti surfaces release increased levels of local bone regulatory factors,
Received in original form January 17, 2012; revised form March 26, 2012; accepted March 30, 2012. Published online April 10, 2012.
Address correspondence to: Barbara D Boyan, PhD, Wallace H. Coulter Department of Biomedical Engineering, Georgia Institute of Technology, 315 Ferst Drive NW,
Atlanta, GA 30332-0363. E-mail: barbara.boyan@bme.gatech.edu
*RON and ALR are co-first authors of this work.
Journal of Bone and Mineral Research, Vol. 27, No. 8, August 2012, pp 1773–1783
DOI: 10.1002/jbmr.1628 ß 2012 American Society for Bone and Mineral Research
1773
including osteoprotegerin (OPG), prostaglandin E2 (PGE2), and transforming growth factor b1 (TGF-b1). These surfacedependent effects are mediated by alpha-2, beta-1 (a2b1) integrin signaling.(6) Osteoblastic differentiation of human mesenchymal stem cells (HMSCs) is also increased on Ti surfaces with micron- and submicron-scale rough topographies, and this is mediated by a2b1 integrin signaling.(7) Taken together, these results indicate that rough Ti substrates promote osteoblast differentiation and maturation more than smooth Ti surfaces.
In addition to surface roughness, surface free energy of Ti substrates also plays a role in regulating bone cell responsiveness. Ti implant surfaces have a low surface free energy due to the adsorption of hydrocarbons and carbonates from the ambient atmosphere onto the TiO2 surface layer. This adsorption also makes the Ti surfaces hydrophobic. Clean TiO2 surfaces are hydrophilic with a high surface free energy,(8) and this can be maintained by limiting exposure to ambient air conditions. MG63 cells cultured on high surface free energy substrates show an enhanced response to Ti surface microtopography. On microrough, high surface free energy Ti substrates, these cells show increases in alkaline phosphatase–specific activity, osteocalcin production, and levels of TGF-b1 and OPG compared to rough Ti surfaces alone.(9)
Human osteoblasts and HMSCs also exhibit enhanced differentiation and osteogenic factor production on the highenergy surfaces.(10,11) Importantly, factors secreted into the conditioned media of osteoblasts grown on the high-energy microtextured Ti surfaces can act on HMSCs cultured on tissue culture polystyrene to induce their osteoblastic differentiation.(7)
These results suggest that peri-implant bone formation in vivo may be modulated by events associated with surface design and that the cells populating the surface will contribute to the periimplant milieu.
In vivo, Ti substrates with a rough microtopography support greater bone-to-implant contact than smooth surfaces do, resulting in greater removal torque strength.(12–14) Preliminary studies have indicated that high surface free energy Ti surfaces have the potential to improve the early stages of soft and hard tissue integration of implants.(15–17) One contributing factor to this may be an increase in vascularization. Both osteoblasts and
HMSCs produce increased levels of angiogenic growth factors including vascular endothelial growth factor A (VEGF-A), basic fibroblast growth factor (FGF-2), and endothelial growth factor
(EGF).(7,10,18) Whether angiogenesis is increased in vivo, however, is not known.
Host bone quality also plays a significant role in determining successful osseointegration. Bone quality and subsequent bone formation can be affected by several factors including smoking, diabetes, cancer, and other diseases.(19,20) Another factor that is known to play a role in bone formation is age. Several studies have shown that both natural bone formation and bone fracture healing in response to osteoinductive factors is impaired in an aged population.(21,22) The results of these studies suggest that new bone formation surrounding Ti implants may also be affected by patient age.
In the present study, osteoblast maturation in response to Ti surface microtopography and surface free energy was assessed with respect to donor age. To do this, osteoblasts were isolated
1774
OLIVARES-NAVARRETE ET AL.
from 1-month, 3-month, and 11-month-old Sprague-Dawley rats, representing young, adult, and old age groups, respectively, and were cultured on Ti substrates with two different surface morphologies and identical morphology but different surface hydrophilicity. In addition, we investigated whether donor age had an effect on the surface-dependent responses to the systemic regulatory hormone 1a,25-dihydroxyvitamin D3
[1a,25(OH)2D3]. To investigate potential mechanisms underlying age-specific differences in cell response, the expression of mRNAs for integrin subunits and receptors for 1a,25(OH)2D3 in osteoblasts derived from young and old populations in response to Ti substrate surface properties was also examined. Finally, the effects of surface microstructure and surface free energy on bone formation and vascularity in vivo were examined using a novel peri-implant bone formation model in which implants were placed in the femoral intramedullary canal of young and old C57BL/6 mice.
Materials and Methods
In vitro studies
Titanium disk preparation
Ti disks (15 mm diameter) were prepared from 1-mm-thick sheets of grade 2 unalloyed Ti as described(23) and were supplied by Institut Straumann AG (Basel, Switzerland). Fabrication methods and resulting morphology of the surfaces have been reported.(8,11,24) Pretreatment (PT) surfaces are smooth, with a mean peak to valley roughness (Ra) of 600 nm. Sandblasted with large grit and acid etched (SLA) surfaces were created from PT disks that were coarse grit–blasted with 0.25 to 0.50 mm corundum until the surface reached a uniform gray tone, followed by acid etching, resulting in a combination of micronand submicron-scale features (Ra ¼ 3.2 mm). Modified SLA
(modSLA) surfaces were created in the same manner as SLA but they were processed with limited exposure to the ambient atmosphere, resulting in a hydrophilic substrate with the same topographical characteristics. modSLA surfaces were rinsed under nitrogen during fabrication and stored in isotonic sodium chloride until use. PT, SLA, and modSLA Ti disks all have a TiO2 surface layer, with the PT and SLA surfaces being hydrophobic due to the adsorption of atmospheric hydrocarbons whereas the modSLA surface is hydrophilic. Advancing contact angles were used to calculate the hydrophilicity of the surfaces as PT
(95.8 degrees), SLA (139.80 degrees), and modSLA ($0 degrees).
Surface free energy for PT, SLA, and modSLA surfaces was calculated according to Zisman (critical surface tension), equation of state (EOS), and geometric mean approaches and have been described in detail elsewhere.(8) Terminal sterilization of all Ti disks was by overnight gamma irradiation at 25 kGy.
Control cultures were grown on standard tissue culture polystyrene (TCPS).
Cell culture
Osteoblasts were isolated from the calvaria (frontal and parietal) bones of 1-month, 3-month, and 11-month-old male SpragueDawley rats using an explant technique.(10,25) Briefly, bones were
Journal of Bone and Mineral Research
cleaned of soft tissue and periosteum. Bones pieces were digested in 0.25% trypsin-EDTA (Invitrogen, Carlsbad, CA, USA) for 15 minutes at 378C to avoid fibroblast contamination. They were then cultured in 100 cm  20 cm Petri dishes (BD
Biosciences, Franklin Lakes, NJ, USA) in DMEM (Cellgro;
Mediatech, Inc., Manassas, VA, USA) supplemented with 10% fetal bovine serum (Hyclone, South Logan, UT, USA) and 1% penicillin-streptomycin (Invitrogen) at 378C, 5% CO2, and 100% humidity. The resulting cultures were subpassaged and seeded on TCPS, PT, SLA, or modSLA substrates at an initial cell density of
20,000 cells/cm2.
Biochemical assays
When cultures reached confluence on TCPS, cells were incubated with media containing either vehicle (0.01% ethanol) or
1 Â 10À7 M 1a,25(OH)2D3 (Enzo Life Sciences, Plymouth Meeting,
PA, USA) for 24 hours. At harvest, cells were released by two sequential 10-minute incubations in 0.25% trypsin-EDTA at 378C.
Cell number was determined using a Z2 Cell Counter (Beckman
Coulter, Fullerton, CA, USA). Cells were lysed in Triton X-100
(Sigma Aldrich, St. Louis, MO, USA) and cellular alkaline phosphatase specific activity measured by assaying the release of p-nitrophenol from p-nitrophenylphosphate at pH 10.2.
Alkaline phosphatase–specific activity was normalized to total protein content of the cell lysates (BCA Protein Assay; Thermo
Fisher Scientific, Waltham, MA, USA).
Levels of secreted factors in the conditioned media were normalized to cell number. Osteocalcin was measured using a commercially available radioimmunoassay following manufacturer’s instructions (Biomedical Technologies, Stoughton, MA,
USA). OPG and VEGF-A were measured using commercially available enzyme-linked immunosorbent assays (ELISA; DuoSet,
R&D Systems, Minneapolis, MN, USA). Active TGF-b1 was measured in the conditioned media using an ELISA kit (DuoSet;
R&D Systems). Media was acidified and total TGF-b1 measured.
Latent TGF-b1 was determined by subtracting active TGF-b1 from total TGF-b1.
(F: 50 -CCAATGATGTGCCTTCTC-30 ; R: 50 -TGTGCCTTCTTCTTCTTC30 ); and the classical vitamin D receptor (VDR) (F: 50 -CATCTTGGCAGTGAGTGAGC-30 ; R: 50 -ACACAACCTACCCATCATCCC-30 ). All genes are presented as normalized to glyceraldehyde 3phosphate dehydrogenase (GAPDH, F: 50 -CATACTCAGCACCAGCATCACC-30 ; R: 50 -AAGTTCAACGGCACAGTCAAGG-30 ).
In vivo study
Titanium implant fabrication and characterization
Bone formation and osseointegration of PT, SLA, and modSLA in vivo were examined using a femoral intramedullary bone formation model. Micro–computed tomography (mCT) imaging of 6-week-old mice was done in order to determine the size of the femoral medullary canal (Fig. 1A, B) and custom-designed Ti implants were manufactured to fit into the femoral medullary space of C57BL/6 mice (Fig. 1C, D). The implants were fabricated from ASTM grade 4 Ti using the same processing methods used for commercially available dental implants. Surface treatments for Ti implants for in vivo studies were prepared in a manner similar to those for Ti surfaces described above. Ti implants consisted of two parts: a handling device and the Ti implant rod
(Fig. 1C–E). The cylindrical Ti implants were manufactured to be
5 mm in length and 0.9 mm in diameter. All implants were sterilized by gamma irradiation at 25 kGy prior to use.
Gene expression
Osteoblasts isolated from 3- and 11-month-old animals were cultured on TCPS or Ti substrates. When cells reached confluence on TCPS, cells were incubated with fresh media for 12 hours. RNA was harvested using a TRIzol (Invitrogen) extraction method. The resulting RNA was quantified (Nanodrop Spectrophotometer;
Thermo Fisher Scientific) and 1 mg RNA was reversed transcribed to cDNA (OmniScript Reverse Transcription Kit; Qiagen, Valencia,
CA, USA) using random oligomers (Promega, Madison, WI, USA).
Starting mRNA quantities were determined using SybrGreen
(BioRad, Hercules, CA, USA) in an iQ5 Real-time PCR machine
(BioRad) and a standard curve method. Expression of mRNA was measured for the following integrin subunits: alpha 2 (ITGA2, F:
50 -ACTGTTCAAGGAGGAGAC-30 ; R: 50 -GGTCAAAGGCTTGTTTAGG30 ); alpha 5 (ITGA5, F: 50 -ATCTGTGTGCCTGACCTG-30 ; R: 50 AAGTTCCCTGGGTGTCTG-30 ); and beta 1 (ITGB1, F: 50 -ATTACTCAGATCCAACCAC-30 ; R: 50 -TCCTCCTCATTTCATTCATC-30 ); as well as for the membrane associated receptor for 1a,25(OH)2D3, protein disulfide isomerase family A, member 3 (PDIA3)(26,27)
Journal of Bone and Mineral Research
Fig. 1. Titanium implant design. Three-dimensional mCT reconstructions of the (A) mouse femoral medullary canal and (B) mCT images of mouse femurs were used to inform implant design. (C) Three-dimensional CAD representation and (D) mechanical drawing showing dimensions of Ti implant with handling device. (E) Image of custom manufactured Ti implant. (F) X-ray image showing an implant that has been inserted into the femoral medullary space without breaking of the bone. (G) Gross morphology of a mouse femur with an implant (arrow).
AGE AND PERI-IMPLANT BONE FORMATION
1775
To characterize the surface morphology of Ti implants, surfaces that were not coated with gold were examined using an Ultra 60 field emission (FE) scanning electron microscope
(SEM; Carl Zeiss SMT Ltd., Cambridge, UK). Images were recorded using a 5-kV accelerating voltage.
Surface wettability of Ti implants was determined with a
´
´
Rame-Hart goniometer (model 250-F1; Rame-Hart Instrument
Co., Mountain Lakes, NJ, USA). Because the Ti implants had a cylindrical shape, it was not possible to measure the surface contact angle directly. Therefore, Ti implant surface wettability was qualitatively determined by immersing Ti implants into ultra-pure water while recording the process. Images were
´
recorded with DROPimage CA software package (Rame-Hart
Instrument Co.).
Surface chemistry was analyzed by using X-ray photoelectron spectroscopy (XPS) on a Thermo K-Alpha (Thermo Fisher
Scientific). XPS was performed using monochromatic Al Ka
X-ray source (hv ¼ 1486.6 eV photons) at a 90-degree takeoff angle in an analysis chamber evacuated to a pressure of
1 Â 10À9 Torr or lower. Data analysis was performed using the
Thermo Advantage 4.43 software package (Thermo Fisher
Scientific).
Surface roughness of Ti implants was characterized by using a
LEXT 3D Material Confocal Laser Microscope (CLM; Olympus
America Inc., Center Valley, PA, USA). Roughness was evaluated using the LEXT OLS4000 software provided by Olympus. Three measurements were made on two implants per surface topography. All measurements were performed in an organic clean room.
Animals
All animal handling and procedures were approved by the
Georgia Institute of Technology Institutional Animal Care and
Use Committee (IACUC), and were conducted in accordance with
NIH guidelines. Custom-made Ti implants were inserted into the femoral medullary canal of mice via a medial parapatellar arthrotomy. Briefly, male C57BL/6 mice (aged 2 months or 9 months) were anesthetized with 5% isoflurane gas inhalation.
The right hind limb was prepared by shaving and cleaning using ethanol and chlorhexidine. Anesthesia was maintained with 2% isoflurane gas inhalation for the duration of the surgical procedure. Cleaned, anesthetized animals were placed in a supine position and were covered with a sterile surgical drape.
Using a scalpel, an 8-mm incision was made over the distal side of the knee. Blunt dissection was used to move aside the ligament and patella to expose the intercondylar notch of the distal femur. Once the femoral cartilage was exposed, a 1-mmround dental bur was used to penetrate the distal intercondylar notch of the femur to access the medullary cavity. A 22-gauge needle was gently pushed into the femur to confirm penetration of the medullary cavity. Cylindrical Ti implants were inserted into the femoral medullary canal and then were broken from the handling device. To confirm successful insertion of the implant into the femoral medullary canal, X-ray imaging was done prior to closure of the surgical incision (Fig. 1F, G). If the Ti implant was not inserted into the medullary canal or if insertion of the Ti implant resulted in a broken femur, the mouse was withdrawn
1776
OLIVARES-NAVARRETE ET AL.
from the study and euthanized using CO2 inhalation. This was done to ensure an appropriate number of successful surgeries for each Ti implant type. Six successful implants were performed for each surface type to ensure adequate sample sizes for statistical analysis as determined by power analysis. Following successful implant insertion, periosteal tissue was closed using resorbable sutures and the surgical incision was closed with wound clips. After recovery from anesthesia, mice were injected with 0.03 mg/kg buprenorphine to relieve postoperative pain.
Animals were monitored every 12 hours for 48 hours postsurgery and once per day thereafter for the duration of the study. Wound clips were removed 10 to 14 days postsurgery. All animals had access to food and water ad libitum for the duration of the study.
Implant harvest and vascular perfusion
Limbs from the 2-month-old mice were harvested 35 days postimplantation. The limbs containing Ti implants were stored in 10% neutral buffered formalin for histological processing.
Limbs from the 9-month-old animals were harvested at 28 days postimplantation for blood vessel quantification and histological analysis. Mice were euthanized via CO2 inhalation. Immediately after death, the thoracic cavity was opened and a 22-gauge butterfly needle was inserted into the left ventricle. The inferior vena cava was severed to allow the vasculature to be flushed.
Heparinized saline (100 U/mL) was used to flush the vasculature followed by perfusion with 10% neutral buffered formalin to fix the tissue specimens. The vasculature was perfused using a radio-opaque silicone rubber compound (Microfil; Flow Tech,
Inc., Carver, MA, USA) mixed in a 9:1 vol/vol ratio with Microfil curing agent. Following vascular perfusion, the injected Microfil compound was allowed to polymerize overnight at 48C before histological processing.
Histology
Fixed limbs were embedded in plastic. Sagittal tissue sections were cut and polished to a final thickness of 10 to 20 mm and were stained with hematoxylin and eosin for histological analysis. Using commercially available image analysis software
(Image-Pro Plus; Media Cybernetics, Bethesda, MD, USA), stained tissue sections were analyzed for bone-to-implant contact (BIC) using two different methods. First, the BIC where the implant surface was in direct contact with the femoral cortical bone surface was calculated for each animal for each implant type and the average total BIC was determined. We also measured the BIC where new bone had formed within the femoral intramedullary space for each animal for each implant surface type.
Statistical analysis
For each in vitro experiment, data presented are mean Æ SEM for six independent cultures per variable. Experiments were repeated to ensure validity. Data are presented from one representative experiment of two experiments. For each in vivo study, six implants were harvested for each implant type. In vitro and in vivo data were analyzed by ANOVA and when statistical differences were detected, Student’s t test for multiple comparisons using Bonferroni’s modification was used. Values of p < 0.05 were considered significant.
Journal of Bone and Mineral Research
Results
In vitro results
Total osteoblast cell number was reduced on all three Ti surfaces compared to TCPS control surfaces for all three donor ages examined (Fig. 2A). On TCPS and PT surfaces, osteoblasts derived from 1-month-old rats had a significantly higher cell number compared to osteoblasts from both 3- and 11-month-old rats while total cell number on SLA surfaces were similar among cells derived from all three age groups. 1a,25(OH)2D3 treatment did not affect cell number on any of the surfaces for any of the ages examined (Fig. 2B).
Alkaline phosphatase–specific activity was higher in osteoblasts of all three age groups on all three Ti surfaces compared to
TCPS (Fig. 2C). The addition of 1a,25(OH)2D3 increased enzyme activity on all surfaces, but the magnitude of the stimulatory effect was donor age dependent (Fig. 2D). Osteoblasts from 11month-old animals did not respond to treatment to the same extent as cells from 1-month or 3-month-old animals. Secreted levels of osteocalcin, which is a late marker of osteoblast maturation, were higher with increased surface roughness and energy for all three age groups examined (Fig. 2E). The increase on SLA and modSLA was significantly less robust in cells from aged animals. 1a,25(OH)2D3 caused a further increase in osteocalcin levels in cultures grown on PT, but this increase was less robust in cells from 11-month-old donors (Fig. 2F).
Local factor production was also sensitive to donor age. In cells from younger animals, OPG levels were higher on all three
Ti surfaces compared to TCPS control surfaces. In cells from
11-month-old animals, OPG levels were increased only in cultures grown on microstructured Ti surfaces (Fig. 3A). The addition of 1a,25(OH)2D3 significantly increased OPG secretion on all surfaces examined, however the effect was donor age–dependent (Fig. 3B). Cells derived from younger donors responded to 1a,25(OH)2D3 to a greater extent than cells derived from the older donors. Similar to OPG production, VEGF-A levels were higher in cultures grown on Ti surfaces compared to TCPS control surfaces in cells from young animals, whereas secreted levels of VEGF-A in cells from 11-month-old animals were only increased on microstructured Ti surfaces (Fig. 3C). 1a,25(OH)2D3 enhanced the stimulated VEGF-A secretion on all surfaces in cultures from 1- and 3-month-old animals but did not have a stimulatory effect in cultures from 11-month-old animals
(Fig. 3D). VEGF-A levels were highest in cells from 3-monthold animals. Active TGF-b1 levels were increased on all three Ti surfaces compared to TCPS in all three age groups. 1a,25(OH)2D3 increased levels of active TGF-b1 in osteoblasts derived from all donor age groups with levels being higher on all three Ti surfaces compared to TCPS control surfaces (Fig. 3F). Latent TGF-b1 levels were higher only in response to growth on microtextured Ti surfaces in cells from 1- and 3-month-old animals whereas levels in cells from 11-month-old animals were unaffected by either Ti surface roughness or energy (Fig. 3G). 1a,25(OH)2D3 increased latent TGF-b1 levels on all surfaces examined and this effect was greatest in cells from younger animals (Fig. 3H).
Expression of integrin receptor subunits a2 and a5 were higher on all three Ti surfaces examined compared to TCPS control surfaces for both 3- and 11-month-old animals; however,
Fig. 2. Response of osteoblasts derived from 1-, 3-, and 11-month-old rats to Ti surface roughness and hydrophilicity and treatment with 1a,25(OH)2D3.
Cells were cultured on TCPS, PT, SLA, and modSLA Ti surfaces with or without 1 Â 10À7 M 1a,25(OH)2D3. (A, D) Cell number and (B, E) alkaline phosphatase specific activity in the cell lysate, and (C, F) osteocalcin levels were determined. Values presented are mean Æ SEM of six independent cultures. Ãp < 0.05 versus TCPS, ^p < 0.05 versus 1-month-old rats.
Journal of Bone and Mineral Research
AGE AND PERI-IMPLANT BONE FORMATION
1777
Fig. 3. Response of osteoblasts derived from 1-, 3-, and 11-month-old rats to Ti surface roughness and hydrophilicity and treatment with 1a,25(OH)2D3.
Cells were cultured on TCPS, PT, SLA, and modSLA Ti surfaces with or without 1 Â 10À7 M 1a,25(OH)2D3. (A, E) Osteoprotegerin, (B, F) VEGF-A, (C, G) active
TGF-b1, and (D, H) latent TGF-b1 levels were determined. Values presented are mean Æ SEM of six independent cultures. Ãp < 0.05 versus TCPS, ^p < 0.05 versus 1-month-old rats.
expression of both integrins a2 and a5 were lower in cells derived from 11-month-old animals on all substrates examined when compared to 3-month-old donor cells (Fig. 4A, B). Levels of b1 integrin mRNA were higher for cells on microrough SLA and microrough, hydrophilic modSLA Ti surfaces compared to TCPS
substrates for cells from both 3- and 11-month-old animals
(Fig. 4C). Expression of the b1 integrin was similar between cells from 3- and 11-month-old animals except on modSLA, where cells from 11-month-old animals displayed a reduction in b1 expression. Fig. 4. Gene expression in adult (3-month-old) and old (11-month-old) rats. Osteoblasts isolated from 3- and 11-month-old rats were cultured on
TCPS and PT, SLA, and modSLA Ti surfaces and expression of Integrin a2 (ITGA2, A), Integrin a5 (ITGA5, B), and Integrin b1 (ITGB1, C) and vitamin D receptors PDIA3 (D) and VDR (E) were measured. Values presented are mean Æ SEM of six independent cultures. Ãp < 0.05 versus TCPS, p < 0.05 versus
3-month-old rats.
1778
OLIVARES-NAVARRETE ET AL.
Journal of Bone and Mineral Research
Receptors for 1a,25(OH)2D3 were expressed in osteoblasts isolated from both young and old donors. Levels of expression were specific to receptor type and varied with the surface and donor age. mRNAs for PDIA3, the membrane receptor for
1,25(OH)2D3, were reduced in response to increasing Ti surface roughness and surface hydrophilicity, but no differences in expression between osteoblasts from the different aged animals were observed (Fig. 4D). In contrast, mRNAs for VDR, the nuclear receptor for 1,25(OH)2D3, increased on SLA and modSLA surfaces compared to TCPS for osteoblasts from both age groups (Fig. 4E). In cell cultures from 11-month-old animals, expression of VDR was significantly higher than that observed in cell cultures from 3-month-old animals on all surfaces examined.
oxygen (O1s), and carbon (C1s) were detected on PT, SLA, and modSLA surfaces (Table 1). Trace nitrogen (N1s) was detected on PT and SLA surfaces. Atomic percentages for the PT, SLA, and modSLA surfaces are summarized in Table 1. More oxygen and titanium with less carbon was found on modSLA surfaces compared to PT and SLA surfaces.
Surface roughness determined by CLM was significantly different between PT (Ra ¼ 0.21 mm) and SLA (Ra ¼ 3.39 mm). In contrast, there was no difference between SLA (Ra ¼ 3.39 mm) and modSLA (Ra ¼ 3.47 mm) (Table 1). SEM and CLM suggest that no morphological difference was observed between SLA and modSLA surfaces. However, higher surface wettability of the modSLA surface than the SLA surface was induced by different surface chemistry.
Implant characterization
The surface morphology of PT, SLA, and modSLA implants was obtained at low and high magnification with SEM (Fig. 5A).
The surfaces of PT implants were relatively smooth with more irregular surface features than SLA and modSLA implants. Both
SLA and modSLA surfaces exhibit complex features such as shallow micron-scale craters (10–60 mm) and submicron-scale pits (1–3 mm). There was no clear boundary between craters and pits. Unmodified areas characterized by flat and smooth sections were also found on SLA and modSLA surfaces. However, there were no observed topographical differences between SLA and modSLA surfaces.
The modSLA surface showed excellent wettability compared to the SLA surface with poor wettability (Fig. 5B). Titanium (Ti2p),
In vivo results
Implant osseointegration was quantified by evaluating transverse histology sections. An example of such a cut is presented in
Fig. 6. The amount of bone and the BIC was different when the implant was in contact with cortical bone compared to bone in the marrow compartment. Accordingly, the morphometric analysis was performed separately on the areas contacting cortical bone versus the bone contact in the marrow area. In both age groups, neither Ti implant surface microstructure nor surface energy had an effect on BIC where the implant surface came in direct contact with the femoral cortical bone surface (Table 2).
Neither Ti surface microstructure nor surface energy had an effect on total marrow to implant contact in young (2-month-old)
Fig. 5. Characterization of implant surfaces. (A) Surface morphology was examined using scanning electron microscopy. (B) Contact angle was determined by immersion in ultra-pure water.
Journal of Bone and Mineral Research
AGE AND PERI-IMPLANT BONE FORMATION
1779
Table 1. Surface Chemical Composition and Roughness Parameters of Titanium Cylinder Surfaces
Concentration
(atomic Æ SD %)
Roughness parameter
(mean Æ SD mm)
Cls
Ols
Ti2p
Ra
Rt
31.7 Æ 2.3
40.3 Æ 1.1
24.8 Æ 2.1
PT
SLA
modSLA
Nls
2.4 Æ 0.1
3.0 Æ 0.4
49.5 Æ 1.2
43.5 Æ 0.7
54.5 Æ 1.5
16.4 Æ 1.0
13.3 Æ 0.7
20.6 Æ 0.6
0.21 Æ 0.03
3.39 Æ 0.63
3.47 Æ 0.71
1.39 Æ 0.32
19.71 Æ 5.09
21.15 Æ 4.96
Values are mean Æ SD.
C1s ¼ carbon; N1s ¼ nitrogen; O1s ¼ oxygen; Ti2p ¼ Titanium; Ra ¼ mean peak to valley roughness; Rt ¼ maximum roughness height; PT ¼ pretreatment; SLA ¼ sandblasted with large grit and acid-etched; modSLA ¼ SLA processed with limited exposure to the ambient atmosphere.
male C57BL/6 mice (Fig. 7A). In 9-month-old male C57BL/6 mice, surface microtopography alone had no significance effect on total BIC within the femoral marrow cavity; however, the BIC was significantly increased in response to the surface microtopography and high surface energy seen on modSLA Ti implants compared to smooth PT Ti implants (Fig. 7A). The total number of blood vessels within the marrow space surrounding Ti implants within the femoral medullary space was also increased in the modSLA implant group relative to the smoother PT controls
(Fig. 7B).
Discussion
The success of implants in compromised patients in general, and in older patients specifically, has attracted research attention.
Several studies have reported conflicting results on whether the healing capacity diminishes with increasing age.(21,22) Endosteal bone formation and marrow regeneration following tibial marrow ablation are delayed with increasing age in immunocompromised rats.(22) Healing of segmental fracture defects was delayed in older animals with demineralized bone matrix (DBM) treatment compared to younger animals.(21) Diminished healing capabilities with increasing age have also been reported in other organ systems. Bone marrow–derived mesenchymal stem cell homing to sites of burn injury was significantly reduced in older animals.(28) In contrast, compensatory bone formation during tooth movement is maintained at similar levels in both young and old rats.(29) The results of the present study indicate that responses of osteoblasts from aged animals to surface roughness and the addition of 1a,25(OH)2D3 as well as in vivo osseointegration in older animals were reduced when compared to younger animals.
Ti implant surface properties are known to affect osteoblast maturation in vitro and new bone formation in vivo. The response of osteoblasts to microstructured Ti surfaces is similar to their response to bone wafer surfaces that have been preconditioned by osteoclasts to create microtextured resorption pits,(30) suggesting that the results of this study may have broader application to our understanding of the role of aging in bone physiology. Consistent with previous results, the present study found that osteoblasts display reduced proliferation and increased maturation in response to increasing surface roughness and surface free energy.(3,5,15,31–33) It was also observed that treatment with the systemic osteotropic hormone 1a,25(OH)2D3
Table 2. Cortical Bone-to-Implant Contact for 8-Week and
9-Month-Old Mice for PT, SLA, and modSLA Ti Implants
Cortical bone-to-implant contact
Surface type
PT
SLA modSLA Fig. 6. Representative histology sections. Representative histology sections PT, SLA, and modSLA titanium implants placed in of (A–C)
2-month-old or (D–F) 9-month-old mice.
1780
OLIVARES-NAVARRETE ET AL.
8-week-old mice
9-month-old mice
0.88 Æ 0.06
0.87 Æ 0.05
0.92 Æ 0.07
0.89 Æ 0.06
0.89 Æ 0.07
0.93 Æ 0.07
Values are mean Æ SD of percent bone-to-implant contact.
PT ¼ pretreatment; SLA ¼ sandblasted with large grit and acid-etched; modSLA ¼ SLA processed with limited exposure to the ambient atmosphere.
Journal of Bone and Mineral Research
Fig. 7. In vivo bone formation. Bone formation and neovascularization surrounding PT, SLA, and modSLA Ti implants was examined using a novel murine intramedullary bone formation model. (A) The percent bone to implant contact (% BIC) was measured for both 2-month-old and 9-month-old animals.
Ã
p < 0.05 versus PT. (B) The total number of blood vessels within the marrow space of 9-month-old animals. Ãp < 0.05 versus PT. Values presented are the mean Æ SEM of six implants per group.
further enhanced osteoblast response to Ti substrate features as has been reported.(34) While osteoblasts isolated from 1-, 3-, and
11-month-old Sprague-Dawley rats showed surface roughness and energy-dependent increases in maturation and local factor production, osteoblasts isolated from 11-month-old animals had a less robust response to both Ti surface roughness properties.
Cells from older animals also had a diminished response to treatment with 1 Â 10À7 M 1a,25(OH)2D3 compared to osteoblasts isolated from 1- and 3-month-old animals.
Our results suggest that integrin signaling may play a role in the reduced response observed in cells from aged rats. We have previously shown that a5b1 is required for osteoblast attachment and proliferation, but a2b1 is required for osteoblast differentiation of HMSCs and osteoblasts.(6,7,35) Expression levels of a2 and a5 as well as b1 were lower in osteoblasts derived from older animals.
Age-dependent differences in expression of PDIA3 were not observed, suggesting that signaling via PDIA3-dependent pathways may not mediate the age-dependent differences in response to 1a,25(OH)2D3. In contrast, osteoblasts from older animals had higher expression of mRNAs for VDR compared to osteoblasts from younger animals. This suggests that the diminished responsiveness of osteoblasts from older animals to treatment with 1a,25(OH)2D3 is not caused by a lack of receptors in these cells but rather by some other mechanism.
Alternatively, increased VDR may be a compensatory mechanism in the older animals. mRNAs for PDIA3 were reduced in osteoblasts cultured on the microtextured surfaces whereas mRNAs for VDR were increased, regardless of the age of the donor rats. We have observed similar changes in expression of these two receptors during osteogenic differentiation of mouse embryoid bodies or cultures of
HMSCs.(36) Embryonic stem cells (ESCs) expressed mRNA and protein for both receptors for 1a,25(OH)2D3 and they continued to be present as the ESCs differentiated in the form of embryoid bodies. Interestingly, the expression of Vdr increased in embryoid bodies after incubation in osteogenic medium, while Pdia3 expression decreased. In adult HMSCs, osteogenic induction increased VDR mRNA whereas levels of PDIA3 mRNA remained stable after osteogenic induction. Taken together with the results of the present study, these findings suggest that expression
Journal of Bone and Mineral Research
levels of these receptors are modulated during the course of osteogenic differentiation, but it is not known if changes in mRNA are required to initiate a change in osteoblast differentiation state or if they are a consequence of that state.
The novel murine intramedullary bone formation model used in this study enabled us to compare BIC and vasculogenesis as a function of age in two different conditions. Injury to the medullary canal caused by insertion of the implant induced endosteal bone formation and with it new blood vessel formation.(37) In the absence of a biomaterial within the canal, the endosteal bone will be remodeled, restoring the contours of the canal within 28 days. The rate and extent of remodeling and the quality of the regenerated marrow are sensitive to biomaterial properties(38) and vary with animal age.(22)
The results of the present study show that both age as well as biomaterial surface features affect osseointegration and the neovasculature, not only in the peri-implant cortical bone but also in the endosteal bone in the medullary canal. In young, skeletally mature C57BL/6 mice, neither Ti surface roughness nor wettability had a significant effect on osseointegration as determined by histological examination of total bone to implant contact at 35 days postimplantation. However, in adult animals smooth and SLA surfaces had less BIC and new blood vessels compared to modSLA. Moreover, BIC and neovasculature in older animals with modSLA implants were comparable to levels found in young animals. modSLA had higher BIC after 4 weeks of implantation compared to SLA.
Age-dependent differences in peri-implant bone formation may be resolved over time. Similar to our results, modSLA implants supported significantly greater BIC compared to SLA implants in minipigs at 14 days postimplantation.(16) It may also be possible that in the young mice, new bone formation around modSLA implants occurs more rapidly than around PT or SLA implants; however, at our harvest time of 35 days postimplantation, these differences may not have been observed.
Our results are consistent with results found previously demonstrating that new bone formation capacity is diminished with age(22) and support the hypothesis that implant surface properties can enhance osseointegration in sites of compromised bone. In 9-month-old C57BL/6 mice, which are an aged model representing compromised bone, the combination of a
AGE AND PERI-IMPLANT BONE FORMATION
1781
rough surface microtopography and high surface energy on modSLA substrates resulted in a significant increase in total bone to implant contact surrounding these implants. In addition, when the vasculature of these animals was perfused and the total number of blood vessels surrounding the implants within the marrow space determined, it was found that modSLA implants had significantly increased total blood vessel number. These results are in agreement with our previous findings in vitro, which indicated that surface roughness enhanced production of angiogenic and vasculogenic factors.(18)
In a clinical setting, establishment of a vasculature preceding or concomitant with bone formation allows for the delivery of oxygen, systemic hormones, and nutrients to the injury site, as well as the migration of mesenchymal stem cells. In the absence of neovascularization, the implant may be surrounded by a fibrous capsule, resulting in implant loosening and ultimately failure, demonstrating the importance of the initial reaction of the first cells to encounter an implanted material. The results from this study have shown that microstructured, hydrophilic
Ti surfaces can improve neovascularization and subsequently implant osseointegration in sites of compromised bone formation, such as in an older patient population.
In addition to the data presented here, this novel mouse model of intramedullary bone formation provides several advantages to evaluate the numerous factors involved in periimplant bone formation. The numerous genetically modified mouse strains readily available, such as vitamin D receptor knockout mice will make it easier to isolate and examine the specific roles of these factors in influencing implant osseointegration, particularly in an aged population.
Conclusions
In the present study, it was determined that osteoblast maturation in response to Ti implant surface roughness and surface free energy diminishes with age. Furthermore, osteoblast responsiveness to the systemic osteotropic hormone
1a,25(OH)2D3 was shown to be reduced in osteoblasts derived from aged animals. However, VDR expression was significantly higher in osteoblasts derived from older animals compared to osteoblasts derived from a younger population, indicating that the diminished responsiveness of cells to treatment with
1a,25(OH)2D3 was not caused by a lack of these vitamin D receptors in these cells. Further, we describe here the development of a novel mouse intramedullary bone formation model and show that both new bone formation and neovascularization are reduced in response to Ti implants in older animals. This effect can be avoided by titanium implants with roughened and high-energy surfaces. Taken together, these results indicate that osteoblast maturation in vitro and new bone formation in vivo are diminished with age, suggesting that these factors should be taken into consideration clinically when selecting appropriate biomaterials.
Disclosures
All authors state that they have no conflicts of interest.
1782
OLIVARES-NAVARRETE ET AL.
Acknowledgments
This study was funded by NIH USPHS AR052102, the ITI
Foundation, and Children’s Healthcare of Atlanta. ALR was supported by funding from Cell and Tissue Engineering (CTEng)
NIH Biotechnology Training Grant (TG GM08433). Implants were provided as a gift from Institut Straumann AG (Basel,
Switzerland). We thank Ms. Sonja Bustamante for her excellent technical help.
Authors’ roles: RON and ZS designed the in vitro studies. RON,
SLH, and DLH performed the in vitro studies. ALR and ZS designed the in vivo studies. JHP performed implant surface characterization. ALR, SLH, and ZS performed in vivo studies.
RON, DLC, BDB, and ZS performed data analysis and interpretation. RON and ALR drafted the manuscript, and all authors have critically revised it. BDB accepts responsibility for the integrity of the data analysis for the work described.
References
1. Ratner BDHA, Schoen FJ, Lemons JE. Biomaterials science: an introduction to materials in medicine. 2nd ed. San Diego: Elsevier
Academic Press; 2004.
2. Ellingsen JE. A study on the mechanism of protein adsorption to TiO2.
Biomaterials. 1991;12(6):593–6.
3. Kieswetter K, Schwartz Z, Dean DD, Boyan BD. The role of implant surface characteristics in the healing of bone. Crit Rev Oral Biol Med.
1996;7(4):329–45.
4. Goto T, Yoshinari M, Kobayashi S, Tanaka T. The initial attachment and subsequent behavior of osteoblastic cells and oral epithelial cells on titanium. Biomed Mater Eng. 2004;14(4):537–44.
5. Martin JY, Schwartz Z, Hummert TW, Schraub DM, Simpson J,
Lankford J Jr, Dean DD, Cochran DL, Boyan BD. Effect of titanium surface roughness on proliferation, differentiation, and protein synthesis of human osteoblast-like cells (MG63). J Biomed Mater Res.
1995;29(3):389–401.
6. Olivares-Navarrete R, Raz P, Zhao G, Chen J, Wieland M, Cochran DL,
Chaudhri RA, Ornoy A, Boyan BD, Schwartz Z. Integrin alpha2beta1 plays a critical role in osteoblast response to micron-scale surface structure and surface energy of titanium substrates. Proc Natl Acad
Sci U S A. 2008;105(41):15767–72.
7. Olivares-Navarrete R, Hyzy SL, Hutton DL, Erdman CP, Wieland M,
Boyan BD, Schwartz Z. Direct and indirect effects of microstructured titanium substrates on the induction of mesenchymal stem cell differentiation towards the osteoblast lineage. Biomaterials. 2010;
31(10):2728–35.
8. Rupp F, Scheideler L, Olshanska N, de Wild M, Wieland M, GeisGerstorfer J. Enhancing surface free energy and hydrophilicity through chemical modification of microstructured titanium implant surfaces. J Biomed Mater Res A. 2006;76(2):323–34.
9. Zhao G, Schwartz Z, Wieland M, Rupp F, Geis-Gerstorfer J, Cochran DL,
Boyan BD. High surface energy enhances cell response to titanium substrate microstructure. J Biomed Mater Res A. 2005;74(1):49–58.
10. Olivares-Navarrete R, Hyzy SL, Chaudhri RA, Zhao G, Boyan BD,
Schwartz Z. Sex dependent regulation of osteoblast response to implant surface properties by systemic hormones. Biol Sex Differ.
2010;1(1):4.
11. Olivares-Navarrete R, Hyzy SL, Park JH, Dunn GR, Haithcock DA,
Wasilewski CE, Boyan BD, Schwartz Z. Mediation of osteogenic differentiation of human mesenchymal stem cells on titanium surfaces by a Wnt-integrin feedback loop. Biomaterials. 2011;
32(27):6399–411.
Journal of Bone and Mineral Research
12. Buser D, Schenk RK, Steinemann S, Fiorellini JP, Fox CH, Stich H.
Influence of surface characteristics on bone integration of titanium implants. A histomorphometric study in miniature pigs. J Biomed
Mater Res. 1991;25(7):889–902.
26. Chen J, Olivares-Navarrete R, Wang Y, Herman TR, Boyan BD,
Schwartz Z. Protein-disulfide isomerase-associated 3 (Pdia3) mediates the membrane response to 1,25-dihydroxyvitamin D3 in osteoblasts. J Biol Chem. 2010;285(47):37041–50.
13. Gotfredsen K, Wennerberg A, Johansson C, Skovgaard LT, HjortingHansen E. Anchorage of TiO2-blasted, HA-coated, and machined implants: an experimental study with rabbits. J Biomed Mater Res.
1995;29(10):1223–31.
27. Wang Y, Chen J, Lee CS, Nizkorodov A, Riemenschneider K, Martin D,
Hyzy S, Schwartz Z, Boyan BD. Disruption of Pdia3 gene results in bone abnormality and affects 1alpha,25-dihydroxy-vitamin
D3-induced rapid activation of PKC. J Steroid Biochem Mol Biol.
2010;121(1–2):257–60.
14. Cochran DL, Schenk RK, Lussi A, Higginbottom FL, Buser D. Bone response to unloaded and loaded titanium implants with a sandblasted and acid-etched surface: a histometric study in the canine mandible. J Biomed Mater Res. 1998;40(1):1–11.
15. Schwarz F, Wieland M, Schwartz Z, Zhao G, Rupp F, Geis-Gerstorfer J,
Schedle A, Broggini N, Bornstein MM, Buser D, Ferguson SJ, Becker J,
Boyan BD, Cochran DL. Potential of chemically modified hydrophilic surface characteristics to support tissue integration of titanium dental implants. J Biomed Mater Res B Appl Biomater. 2009;88(2):
544–57.
16. Buser D, Broggini N, Wieland M, Schenk RK, Denzer AJ, Cochran DL,
Hoffmann B, Lussi A, Steinemann SG. Enhanced bone apposition to a chemically modified SLA titanium surface. J Dent Res. 2004;83(7):
529–33.
17. Ferguson SJ, Broggini N, Wieland M, de Wild M, Rupp F, GeisGerstorfer J, Cochran DL, Buser D. Biomechanical evaluation of the interfacial strength of a chemically modified sandblasted and acidetched titanium surface. J Biomed Mater Res A. 2006;78(2):291–7.
18. Raines AL, Olivares-Navarrete R, Wieland M, Cochran DL, Schwartz Z,
Boyan BD. Regulation of angiogenesis during osseointegration by titanium surface microstructure and energy. Biomaterials. 2010;
31(18):4909–17.
19. Kumar A, Jaffin RA, Berman C. The effect of smoking on achieving osseointegration of surface-modified implants: a clinical report. Int J
Oral Maxillofac Implants. 2002;17(6):816–9.
20. Cochran DL. A comparison of endosseous dental implant surfaces.
J Periodontol. 1999;70(12):1523–39.
21. Tucci M, Lancaster R, Wingerter S, Woodall J Jr, Russell G, Benghuzzi
H. Comparison of segmental fracture healing in young and old rats that were treated with bone stimulators - biomed 2009. Biomed Sci
Instrum. 2009;45:407–12.
22. Fisher M, Hyzy S, Guldberg RE, Schwartz Z, Boyan BD. Regeneration of bone marrow after tibial ablation in immunocompromised rats is age dependent. Bone. 2010;46(2):396–401.
23. Zinger O, Zhao G, Schwartz Z, Simpson J, Wieland M, Landolt D,
Boyan B. Differential regulation of osteoblasts by substrate microstructural features. Biomaterials. 2005;26(14):1837–47.
24. Zhao G, Raines AL, Wieland M, Schwartz Z, Boyan BD. Requirement for both micron- and submicron scale structure for synergistic responses of osteoblasts to substrate surface energy and topography. Biomaterials. 2007;28(18):2821–9.
25. Bellows CG, Aubin JE, Heersche JN, Antosz ME. Mineralized bone nodules formed in vitro from enzymatically released rat calvaria cell populations. Calcif Tissue Int. 1986;38(3):143–54.
Journal of Bone and Mineral Research
28. Zhang X, Sarkar K, Rey S, Sebastian R, Andrikopoulou E, Marti GP, FoxTalbot K, Semenza GL, Harmon JW. Aging impairs the mobilization and homing of bone marrow-derived angiogenic cells to burn wounds. J Mol Med (Berl). 2011 Oct; 89(10):985–95.
29. Shimpo S, Horiguchi Y, Nakamura Y, Lee M, Oikawa T, Noda K,
Kuwahara Y, Kawasaki K. Compensatory bone formation in young and old rats during tooth movement. Eur J Orthod. 2003;25(1):
1–7.
30. Boyan BD, Schwartz Z, Lohmann CH, Sylvia VL, Cochran DL, Dean DD,
Puzas JE. Pretreatment of bone with osteoclasts affects phenotypic expression of osteoblast-like cells. J Orthop Res. 2003;21(4):
638–47.
31. Boyan BD, Hummert TW, Dean DD, Schwartz Z. Role of material surfaces in regulating bone and cartilage cell response. Biomaterials.
1996;17(2):137–46.
32. Boyan BD, Lossdorfer S, Wang L, Zhao G, Lohmann CH, Cochran DL,
Schwartz Z. Osteoblasts generate an osteogenic microenvironment when grown on surfaces with rough microtopographies. Eur Cell
Mater. 2003;6:22–7.
33. Zhao G, Zinger O, Schwartz Z, Wieland M, Landolt D, Boyan BD.
Osteoblast-like cells are sensitive to submicron-scale surface structure. Clin Oral Implants Res. 2006;17(3):258–64.
34. Schwartz Z, Lohmann CH, Vocke AK, Sylvia VL, Cochran DL, Dean DD,
Boyan BD. Osteoblast response to titanium surface roughness and
1alpha,25-(OH)(2)D(3) is mediated through the mitogen-activated protein kinase (MAPK) pathway. J Biomed Mater Res. 2001;56(3):
417–26.
35. Keselowsky BG, Wang L, Schwartz Z, Garcia AJ, Boyan BD. Integrin alpha(5) controls osteoblastic proliferation and differentiation responses to titanium substrates presenting different roughness characteristics in a roughness independent manner. J Biomed Mater
Res A. 2007;80(3):700–10.
36. Olivares-Navarrete R, Sutha K, Hyzy SL, Hutton DL, Schwartz Z,
McDevitt T, Boyan BD. Osteogenic differentiation of stem cells alters vitamin D receptor expression. Stem Cells Dev. Epub. 2012 Jan 4.
37. Raines AL, Sunwoo M, Gertzman AA, Thacker K, Guldberg RE,
Schwartz Z, Boyan BD. Hyaluronic acid stimulates neovascularization during the regeneration of bone marrow after ablation. J Biomed
Mater Res A. 2011;96(3):575–83.
38. Schwartz Z, Doukarsky-Marx T, Nasatzky E, Goultschin J, Ranly DM,
Greenspan DC, Sela J, Boyan BD. Differential effects of bone graft substitutes on regeneration of bone marrow. Clin Oral Implants Res.
2008;19(12):1233–45.